Aliphatic TPU film for laminated glass for PPF

  • BASIC PHYSICAL PERFORMANCE
TPU Film have simple molecular structure ( including only C.H.O.N ), TPU doesn't pollute the air while burning and incinerating and will be degraded naturally within 3~5 years under the action of humidity and microorganism after being buried in soil, so it is a good substitute of PVC products and a main-stream product for environmental production.
TPU vs PVB TPU strengths:
Good adhersion to PC/PET and glass as well
No plasticizers
No senstive to water and other chemical so no need for edge seal
No need for refrigerated storage
Less bubbles between substrates during lamination

 

Advantages
Excellent clarity
Super UV resistance, non yellowing
Excellent low temperature flexibility
Excellent Adhesion To Common Laminate Materials
No plasticizer, no attack to PC sheet
Low melting point

 

Military and security
Specialty Laminations
    Touch Screens
    Privacy Screens

 

Description:
Thermoplastic polyurethane , aliphatic polyether .

 

Typical application :
Glass lamination optical interlayer film .

 

ITEM NO.XGT-L100-2PET
SPEC
PET film(50±2µm)
    TPU FILM(100±5%µm)
PET film(75±2µm)
 /
LOT NO.20210315003GRADEA
 ITEMUNITSTANDRADVALUETEST
METHOD
Physical PropertiesTPU film thicknessµm100±5%101ASTM D374
UV b value/<0.40.30ASTM E313
Max ForceN>150185.59ASTM D412
Tensile strengthMpa>4070.94ASTM D412
Elongation at break%>400567.72ASTM D412
100 modulusMpa>59.19ASTM D412
300 modulusMpa>1227.37ASTM D412
Release force (PET 50±2µm)gf/inch/8.71180° Peeling
Release force (PET 75±2µm)gf/inch/15.06

ITEM NO.XGT-L130-2PET
SPEC
PET film(50±2µm)
TPU FILM(130±5%µm)
PET film(75±2µm)
 /
LOT NO.20210316013GRADEA
 ITEMUNITSTANDRADVALUETEST
METHOD
Physical PropertiesTPU film thicknessµm130±5%132ASTM D374
UV b value/<0.40.33ASTM E313
Max ForceN>150242.4ASTM D412
Tensile strengthMpa>4072.29ASTM D412
Elongation at break%>400584.06ASTM D412
100 modulusMpa>59.43ASTM D412
300 modulusMpa>1227.60ASTM D412
Release force
(PET 50±2µm)
gf/inch/8.71180° Peeling
Release force
(PET 75±2µm)
gf/inch/14.20 

ITEM NO.XGT-L150-2PET
SPEC
PET film(50±2µm)
TPU FILM(150±5%µm)
PET film(75±2µm)
 /
LOT NO.20210322058GRADEA
 ITEMUNITSTANDRADVALUETEST
METHOD
Physical PropertiesTPU film thicknessµm150±5%152ASTM D374
UV b value/<0.400.33ASTM E313
Max ForceN>150268.81ASTM D412
Tensile strengthMpa>4068.71ASTM D412
Elongation at break%>400598.33ASTM D412
100 modulusMpa>57.55ASTM D412
300 modulusMpa>1223.25ASTM D412
Release force (PET 50±2µm)gf/inch/6.50 180° Peeling
Release force (PET 75±2µm)gf/inch/11.21 

ITEM NO.XGT-L175-2PET
SPEC
PET film(50±2µm)
TPU FILM(175±5%µm)
PET film(75±2µm)
 /
LOT NO.20210321040GRADEA
 ITEMUNITSTANDRADVALUETEST
METHOD
Physical PropertiesTPU film thicknessµm175±5%175ASTM D374
UV b value/<0.400.37ASTM E313
Max ForceN>150299.7ASTM D412
Tensile strengthMpa>4066.66ASTM D412
Elongation at break%>400577.79ASTM D412
100 modulusMpa>58.44ASTM D412
300 modulusMpa>1224.99ASTM D412
Release force (PET 50±2µm)gf/inch/6.00 180° Peeling
Release force (PET 75±2µm)gf/inch/18.85 

ITEM NO.XGT-L200-2PET
SPEC
PET film(50±2µm)
TPU FILM(200±5%µm)
PET film(75±2µm)
 /
LOT NO.20210321040GRADEA
 ITEMUNITSTANDRADVALUETEST
METHOD
Physical PropertiesTPU film thicknessµm200±5%200ASTM D374
UV b value/<0.400.27ASTM E313
Max ForceN>150259.8ASTM D412
Tensile strengthMpa>4051.1ASTM D412
Elongation at break%>400608.7ASTM D412
100 modulusMpa>57.7ASTM D412
300 modulusMpa>1219.1ASTM D412
Release force (PET 50±2µm)gf/inch/5.60 180° Peeling
Release force (PET 75±2µm)gf/inch/11.20 