Aliphatic TPU Film For PPF

  • BASIC PHYSICAL PERFORMANCE
Descriptions
It is a high performance Aliphatic thermoplastic polyurethane film used for surface protection, which has good mechanical properties, excellent ultraviolet resistance, high transparency and high gloss. This film has been specially developed for protecting susceptible areas of cars and other vehicles from damage of stone chips and scuffing.

Film with excellent abrasion resistance low temperature flexibility and cold-crack resistant
No additives inside, halogen-free and Phthalate-Free Film with excellent adhesive compatibility and printability

Product Size
ITEM NO.Thickness (um)Width*Length (m)Weight (kg)
XGT-L100-2PET1001.55*1000460
XGT-L130-2PET1301.55*810410
XGT-L150-2PET1501.55*810435
XGT-L175-2PET1751.55*750435
XGT-L200-2PET2001.55*670420

Typical Physical Properties
PropertyValueUnitTest method
Hardness90shore AASTM D2240
Tensile strength
>40
MPaASTM D412
Elongation at break
>400
%ASTM D412
Light transmission92%ASTM D1003
Gloss 60°82 ASTM D1003
UV resistanceNo change at 3000 hours A11

ITEM NO.XGT-L100-2PET
SPECPET film(50±2µm)
TPU FILM(100±5%µm)
PET film(75±2µm)
 /
LOT NO.
20210315003
GRADE
A
 
ITEM
UNIT
STANDRAD
VALUE
TEST METHOD
Physical PropertiesTPU film thicknessµm100±5%101ASTM D374
UV b value/<0.40.30ASTM E313
Max ForceN>150185.59ASTM D412
Tensile strengthMpa>4070.94ASTM D412
Elongation at break%>400567.72ASTM D412
100 modulusMpa>59.19ASTM D412
300 modulusMpa>1227.37ASTM D412
Release force (PET 50±2µm)gf/inch/8.71180° Peeling
Release force (PET 75±2µm)gf/inch/15.06

ITEM NO.
XGT-L130-2PET

 

SPEC

 

PET film(50±2µm)
TPU FILM(130±5%µm) PET film(75±2µm)
 
/
LOT NO.
20210316013
GRADE
A
 
ITEM
UNIT
STANDRAD
VALUE
TEST METHOD

 

Physical Properties

 

 

 

 

TPU film thickness
µm
130±5%
132
ASTM D374
UV b value
/
<0.4
0.33
ASTM E313
Max Force
N
>150
242.40
ASTM D412
Tensile strength
Mpa
>40
72.29
ASTM D412
Elongation at break

 

%
>400
584.06
ASTM D412
100 modulus
Mpa
>5
9.43
ASTM D412
300 modulus
Mpa
>12
27.60
ASTM D412
Release force
(PET 50±2µm)
gf/inch
/
5.46

 

180° Peeling
Release force
(PET 75±2µm)
gf/inch
/
14.20

ITEM NO.
XGT-L150-2PET

 

SPEC

 

PET film(50±2µm)
TPU FILM(150±5%µm) PET film(75±2µm)
 
/
LOT NO.
20210322058
GRADE
A
 
ITEM
UNIT
STANDRAD
VALUE
TEST METHOD
Physical Properties

 

 

 

 

 

TPU film thickness
µm
150±5%
152
ASTM D374
UV b value
/
<0.40
0.33
ASTM E313
Max Force
N
>150
268.81
ASTM D412
Tensile strength
Mpa
>40
68.71
ASTM D412
Elongation at break

 

%
>400
598.33
ASTM D412
100 modulus
Mpa
>5
7.55
ASTM D412
300 modulus
Mpa
>12
23.25
ASTM D412
Release force
(PET 50±2µm)
gf/inch
/
6.50

 

180° Peeling
Release force
(PET 75±2µm)
gf/inch
/
11.21

ITEM NO.
XGT-L175-2PET

 

SPEC

 

PET film(50±2µm)
TPU FILM(175±5%µm) PET film(75±2µm)
 
/
LOT NO.
20210321040
GRADE
A
 
ITEM
UNIT
STANDRAD
VALUE
TEST METHOD

 

Physical Properties

 

 

 

 

 

TPU film thickness
µm
175±5%
175
ASTM D374
UV b value
/
<0.40
0.37
ASTM E313
Max Force
N
>150
299.70
ASTM D412
Tensile strength
Mpa
>40
66.66
ASTM D412
Elongation at break

 

%
>400
577.79
ASTM D412
100 modulus
Mpa
>5
8.44
ASTM D412
300 modulus
Mpa
>12
24.99
ASTM D412
Release force
(PET 50±2µm)
gf/inch
/
6.00

 

180° Peeling
Release force
(PET 75±2µm)
gf/inch
/
18.85

ITEM NO.
XGT-L200-2PET

 

SPEC
PET film(50±2µm)
TPU FILM(200±5%µm) PET film(75±2µm)
 
/
LOT NO.
20210321040
GRADE
A
 
ITEM
UNIT
STANDRAD
VALUE
TEST METHOD

 

Physical Properties

 

 

 

 

 

 

TPU film thickness
µm
200±5%
200
ASTM D374
UV b value
/
<0.40
0.27
ASTM E313
Max Force
N
>150
259.8
ASTM D412
Tensile strength
Mpa
>40
51.1
ASTM D412
Elongation at break

 

%
>400
608.7
ASTM D412
100 modulus
Mpa
>5
7.7
ASTM D412
300 modulus
Mpa
>12
19.1
ASTM D412
Release force
(PET 50±2µm)
gf/inch
/
5.6

 

180° Peeling
Release force
(PET 75±2µm)
gf/inch
/
11.2
top Inquiry