Aliphatic TPU Film For PPF_Shanghai Functech Co., Ltd

BASIC PHYSICAL PERFORMANCE

Descriptions

It is a high performance Aliphatic thermoplastic polyurethane film used for surface protection, which has good mechanical properties, excellent ultraviolet resistance, high transparency and high gloss. This film has been specially developed for protecting susceptible areas of cars and other vehicles from damage of stone chips and scuffing.

Film with excellent abrasion resistance low temperature flexibility and cold-crack resistant

No additives inside, halogen-free and Phthalate-Free Film with excellent adhesive compatibility and printability

Product Size

ITEM NO.	Thickness (um)	*WidthLength (m)**	Weight (kg)
XGT-L100-2PET	100	1.55*1000	460
XGT-L130-2PET	130	1.55*810	410
XGT-L150-2PET	150	1.55*810	435
XGT-L175-2PET	175	1.55*750	435
XGT-L200-2PET	200	1.55*670	420

Typical Physical Properties

Property	Value	Unit	Test method
Hardness	90	shore A	ASTM D2240
Tensile strength	>40	MPa	ASTM D412
Elongation at break	>400	%	ASTM D412
Light transmission	92	%	ASTM D1003
Gloss 60°	82		ASTM D1003
UV resistance	No change at 3000 hours		A11

ITEM NO.	XGT-L100-2PET
SPEC	PET film（50±2µm） TPU FILM（100±5%µm） PET film（75±2µm）
	/
LOT NO.	20210315003			GRADE	A
	ITEM	UNIT	STANDRAD	VALUE	TEST METHOD
Physical Properties	TPU film thickness	µm	100±5%	101	ASTM D374
	UV b value	/	<0.4	0.30	ASTM E313
	Max Force	N	>150	185.59	ASTM D412
	Tensile strength	Mpa	>40	70.94	ASTM D412
	Elongation at break	%	>400	567.72	ASTM D412
	100 modulus	Mpa	>5	9.19	ASTM D412
	300 modulus	Mpa	>12	27.37	ASTM D412
	Release force (PET 50±2µm)	gf/inch	/	8.71	180° Peeling
	Release force (PET 75±2µm)	gf/inch	/	15.06	180° Peeling

ITEM NO.	XGT-L130-2PET
SPEC	PET film（50±2µm） TPU FILM（130±5%µm） PET film（75±2µm）
	/
LOT NO.	20210316013			GRADE	A
	ITEM	UNIT	STANDRAD	VALUE	TEST METHOD
Physical Properties	TPU film thickness	µm	130±5%	132	ASTM D374
	UV b value	/	<0.4	0.33	ASTM E313
	Max Force	N	>150	242.40	ASTM D412
	Tensile strength	Mpa	>40	72.29	ASTM D412
	Elongation at break	%	>400	584.06	ASTM D412
	100 modulus	Mpa	>5	9.43	ASTM D412
	300 modulus	Mpa	>12	27.60	ASTM D412
	Release force (PET 50±2µm)	gf/inch	/	5.46	180° Peeling
	Release force (PET 75±2µm)	gf/inch	/	14.20	180° Peeling

ITEM NO.	XGT-L150-2PET
SPEC	PET film（50±2µm） TPU FILM（150±5%µm） PET film（75±2µm）
	/
LOT NO.	20210322058			GRADE	A
	ITEM	UNIT	STANDRAD	VALUE	TEST METHOD
Physical Properties	TPU film thickness	µm	150±5%	152	ASTM D374
	UV b value	/	<0.40	0.33	ASTM E313
	Max Force	N	>150	268.81	ASTM D412
	Tensile strength	Mpa	>40	68.71	ASTM D412
	Elongation at break	%	>400	598.33	ASTM D412
	100 modulus	Mpa	>5	7.55	ASTM D412
	300 modulus	Mpa	>12	23.25	ASTM D412
	Release force (PET 50±2µm)	gf/inch	/	6.50	180° Peeling
	Release force (PET 75±2µm)	gf/inch	/	11.21	180° Peeling

ITEM NO.	XGT-L175-2PET
SPEC	PET film（50±2µm） TPU FILM（175±5%µm） PET film（75±2µm）
	/
LOT NO.	20210321040			GRADE	A
	ITEM	UNIT	STANDRAD	VALUE	TEST METHOD
Physical Properties	TPU film thickness	µm	175±5%	175	ASTM D374
	UV b value	/	<0.40	0.37	ASTM E313
	Max Force	N	>150	299.70	ASTM D412
	Tensile strength	Mpa	>40	66.66	ASTM D412
	Elongation at break	%	>400	577.79	ASTM D412
	100 modulus	Mpa	>5	8.44	ASTM D412
	300 modulus	Mpa	>12	24.99	ASTM D412
	Release force (PET 50±2µm)	gf/inch	/	6.00	180° Peeling
	Release force (PET 75±2µm)	gf/inch	/	18.85	180° Peeling

ITEM NO.	XGT-L200-2PET
SPEC	PET film（50±2µm） TPU FILM（200±5%µm） PET film（75±2µm）
	/
LOT NO.	20210321040			GRADE	A
	ITEM	UNIT	STANDRAD	VALUE	TEST METHOD
Physical Properties	TPU film thickness	µm	200±5%	200	ASTM D374
	UV b value	/	<0.40	0.27	ASTM E313
	Max Force	N	>150	259.8	ASTM D412
	Tensile strength	Mpa	>40	51.1	ASTM D412
	Elongation at break	%	>400	608.7	ASTM D412
	100 modulus	Mpa	>5	7.7	ASTM D412
	300 modulus	Mpa	>12	19.1	ASTM D412
	Release force (PET 50±2µm)	gf/inch	/	5.6	180° Peeling
	Release force (PET 75±2µm)	gf/inch	/	11.2	180° Peeling