TPU Film have simple molecular structure ( including only C.H.O.N ), TPU doesn't pollute the air while burning and incinerating and will be degraded naturally within 3~5 years under the action of humidity and microorganism after being buried in soil, so it is a good substitute of PVC products and a main-stream product for environmental production.
TPU vs PVB TPU strengths:
Good adhersion to PC/PET and glass as well
No plasticizers
No senstive to water and other chemical so no need for edge seal
No need for refrigerated storage
Less bubbles between substrates during lamination
Advantages
Excellent clarity
Super UV resistance, non yellowing
Excellent low temperature flexibility
Excellent Adhesion To Common Laminate Materials
No plasticizer, no attack to PC sheet
Low melting point
Military and security
Specialty Laminations
Touch Screens
Privacy Screens
Description:
Thermoplastic polyurethane , aliphatic polyether .
Typical application :
Glass lamination optical interlayer film .
| ITEM NO. | XGT-L100-2PET | ||||
| SPEC | 
PET film（50±2µm） TPU FILM（100±5%µm） PET film（75±2µm） | ||||
| / | |||||
| LOT NO. | 20210315003 | GRADE | A | ||
| ITEM | UNIT | STANDRAD | VALUE |
TEST METHOD | |
| Physical Properties | TPU film thickness | µm | 100±5% | 101 | ASTM D374 |
| UV b value | / | <0.4 | 0.30 | ASTM E313 | |
| Max Force | N | >150 | 185.59 | ASTM D412 | |
| Tensile strength | Mpa | >40 | 70.94 | ASTM D412 | |
| Elongation at break | % | >400 | 567.72 | ASTM D412 | |
| 100 modulus | Mpa | >5 | 9.19 | ASTM D412 | |
| 300 modulus | Mpa | >12 | 27.37 | ASTM D412 | |
| Release force (PET 50±2µm) | gf/inch | / | 8.71 | 180° Peeling | |
| Release force (PET 75±2µm) | gf/inch | / | 15.06 | ||
| ITEM NO. | XGT-L130-2PET | ||||
| SPEC |
PET film（50±2µm） TPU FILM（130±5%µm） PET film（75±2µm） | ||||
| / | |||||
| LOT NO. | 20210316013 | GRADE | A | ||
| ITEM | UNIT | STANDRAD | VALUE |
TEST METHOD | |
| Physical Properties | TPU film thickness | µm | 130±5% | 132 | ASTM D374 |
| UV b value | / | <0.4 | 0.33 | ASTM E313 | |
| Max Force | N | >150 | 242.4 | ASTM D412 | |
| Tensile strength | Mpa | >40 | 72.29 | ASTM D412 | |
| Elongation at break | % | >400 | 584.06 | ASTM D412 | |
| 100 modulus | Mpa | >5 | 9.43 | ASTM D412 | |
| 300 modulus | Mpa | >12 | 27.60 | ASTM D412 | |
|
Release force (PET 50±2µm) | gf/inch | / | 8.71 | 180° Peeling | |
|
Release force (PET 75±2µm) | gf/inch | / | 14.20 | ||
| ITEM NO. | XGT-L150-2PET | ||||
| SPEC |
PET film（50±2µm） TPU FILM（150±5%µm） PET film（75±2µm） | ||||
| / | |||||
| LOT NO. | 20210322058 | GRADE | A | ||
| ITEM | UNIT | STANDRAD | VALUE |
TEST METHOD | |
| Physical Properties | TPU film thickness | µm | 150±5% | 152 | ASTM D374 |
| UV b value | / | <0.40 | 0.33 | ASTM E313 | |
| Max Force | N | >150 | 268.81 | ASTM D412 | |
| Tensile strength | Mpa | >40 | 68.71 | ASTM D412 | |
| Elongation at break | % | >400 | 598.33 | ASTM D412 | |
| 100 modulus | Mpa | >5 | 7.55 | ASTM D412 | |
| 300 modulus | Mpa | >12 | 23.25 | ASTM D412 | |
| Release force (PET 50±2µm) | gf/inch | / | 6.50 | 180° Peeling | |
| Release force (PET 75±2µm) | gf/inch | / | 11.21 | ||
| ITEM NO. | XGT-L175-2PET | ||||
| SPEC |
PET film（50±2µm） TPU FILM（175±5%µm） PET film（75±2µm） | ||||
| / | |||||
| LOT NO. | 20210321040 | GRADE | A | ||
| ITEM | UNIT | STANDRAD | VALUE |
TEST METHOD | |
| Physical Properties | TPU film thickness | µm | 175±5% | 175 | ASTM D374 |
| UV b value | / | <0.40 | 0.37 | ASTM E313 | |
| Max Force | N | >150 | 299.7 | ASTM D412 | |
| Tensile strength | Mpa | >40 | 66.66 | ASTM D412 | |
| Elongation at break | % | >400 | 577.79 | ASTM D412 | |
| 100 modulus | Mpa | >5 | 8.44 | ASTM D412 | |
| 300 modulus | Mpa | >12 | 24.99 | ASTM D412 | |
| Release force (PET 50±2µm) | gf/inch | / | 6.00 | 180° Peeling | |
| Release force (PET 75±2µm) | gf/inch | / | 18.85 | ||
| ITEM NO. | XGT-L200-2PET | ||||
| SPEC |
PET film（50±2µm） TPU FILM（200±5%µm） PET film（75±2µm） | ||||
| / | |||||
| LOT NO. | 20210321040 | GRADE | A | ||
| ITEM | UNIT | STANDRAD | VALUE |
TEST METHOD | |
| Physical Properties | TPU film thickness | µm | 200±5% | 200 | ASTM D374 |
| UV b value | / | <0.40 | 0.27 | ASTM E313 | |
| Max Force | N | >150 | 259.8 | ASTM D412 | |
| Tensile strength | Mpa | >40 | 51.1 | ASTM D412 | |
| Elongation at break | % | >400 | 608.7 | ASTM D412 | |
| 100 modulus | Mpa | >5 | 7.7 | ASTM D412 | |
| 300 modulus | Mpa | >12 | 19.1 | ASTM D412 | |
| Release force (PET 50±2µm) | gf/inch | / | 5.60 | 180° Peeling | |
| Release force (PET 75±2µm) | gf/inch | / |
11.20 | ||